Products
- Chemical Auxiliary Agent[3]
- Alkali[6]
- Carbonate[2]
- Bath Mats[1]
- Welding Fluxes[10]
- Carpet[10]
- Mat[2]
Contact Us
- Contact Person : Mr. Xu Ricky
- Company Name : Shandong Laiwu Cn-Aihua Carpet Co., Ltd.
- Tel : 86-0634-6219317
- Fax : 86-0634-6219012
- Address : Shandong,Laiwu,RenHuaYuan industrial Park
- Country/Region : China
- Zip : 271100
Product Detailed
Related Categories:Welding Fluxes
Related Product Searches:sintered welding flux ZT.SJ101G,High Quality,sintered welding flux ZT.SJ101G , welding flux for electrode,ZT SJ101G
sintered welding flux ZT.SJ101G :
In accordance with GB/F4A4-H08C F5A4-H10Mn2
Equivalent to AWS F7A4
Related Product Searches:sintered welding flux ZT.SJ101G,High Quality,sintered welding flux ZT.SJ101G , welding flux for electrode,ZT SJ101G
ZT.SJ101G(welding flux)
In accordance with GB/F4A4-H08C F5A4-H10Mn2Equivalent to AWS F7A4 DESCRIPTION: ZT.SJ101G is a kind of special agglomerated flux that have been designed used in welding lose oil and lose gas steel tube. Alkalinity 1.8, it is grey spherical pellet,size 2.0-0.4(10-45 mesh). Under alternating current and the condition of direct current, it can be used. If welding wire joins positive electrode, the speed of welding can reach 90M-120M, Electric arc is stabilized, is easy to remove to weld dregs, join position smooth. Join metal have the higher impact tenacity in low temperature.The flux with good fight tide performance, pellet strength, can satisfy normal transportation store, circulates to use. Among welding course the consumption of welding flux has less quantity. APPLICATIONS: In combination with H08C,H08MnA,H10Mn2,h08MnMoA,H08Mn2MoA wires, It is suitable for welding various pipeline steel material, such as X52,X60,X65,X70,also be used in multilayer welding , two-sided only road welding, welding electrodes welding, narrow gap bury arc welding voluntarily. TYPICAL FLUX COMPOSITION RANGE:(%)SiO2+TiO2 | CaO+MgO | Al2O3+MnO | CaF2 | S | P |
18-25 | 28-35 | 23-30 | 16-25 | ≤0.06 | ≤0.08 |
With weldingwire | ósMPa | óbMPa | 5% | Akv(J) | |
-20°C | -40°C | ||||
H10Mn2 | ≥400 | 490-660 | ≥22 | ≥120 | ≥90 |
H08C | ≥400 | 600-650 | ≥22 | ≥80 | ≥34 |
sintered welding flux ZT.SJ101G